Welcome to  http://www.cgstape.com                                                                       1-877-828-8898
 

Best Source For: Fiberglass Sleeving and Fiberglass Tape

 >Polyimide Adhesive Tape

   -1 mil Polyimide Tape

   -2 mil Polyimide Tape

   -5 mil Polyimide Tape

   -linered Polyimide Tape

   -Hi-Temp Polyimide Discs

   -ESD Polyimide Tape

   -Black Polyimide Tape

   -White Polyimide Lable

 >Polyimide Film

   -HN Polyimide Film

   -FN Polyimide Film

   -CM Polyimide Film

   -MT Polyimide Film

   -CR Polyimide Film

   -Black Polyimide Film

 >Polyimide Composite

   -NKN Polyimide Composite

 >PTFE Adhesive Tape

 >Polyester Tape

 >Fiberglass Products

   -Glass Cloth Tape

   -Fiberglass Tape

   -Glass Filament Tape

   -Fiberglass Sleeving

 >Company Profile

 >Contact Info

 >Electric-brochure

 

 

 

 

 

 

 

 

 

 

 

 

 

 

 

 

 

 

 

 

 

 

 

 

 

 

 

 

 

 

 

 

 

 

 

 

 

 

 

 

 

 

 

 

 

 

 

 

 

 

 

 

 

 

Fiberglass Sleeving

FSG FLEXIBLE & SELF-EXTINGUISHABLE SILICONE SLEEVE

DESCRIPTION:

  The flexible and self-extinguishable silicone glassfiber sleeving FSG series made by our company is braided with nonalkali fiberglass, it is treated at a high temperature and coated with a special kind of silicone resin.

  This flexible and self-extinguishable silicone glassfiber sleeving possesses good qualities of dielectric, self-extinguishment, excellent softness. It is widely used as wiring insulator for H grade electrical mechinery, domestic electrical appliances, heating electric equipments and electronic apparatus, and also for the protection of collected strands of wire.
  Colour: Natural, we also make sleeves of different colours needed by the users. Sleeve FSG series possesses good flexibility and self-extinguishment.

Specification

Type Name Dielectric Endurance to Resistance to Volume
grades temperature burning resistivity    
FSG-1 Flexible self-extinguishable silicone glassfiber sleeve C2 200℃(-70℃) UL1441 10″Ωcm
FSG-2 Flexible self-extinguishable silicone glassfiber sleeve C1 200℃(-70℃) UL1441 10″Ωcm
FSG-3 Flexible self-extinguishable silicone glassfiber sleeve B 200℃(-70℃) UL1441 10″Ωcm
FSG-3A Flexible self-extinguishable silicone glassfiber sleeve A 200℃(-70℃) UL1441 10″Ωcm

Size(mm)

Inside Diametre Wall Thickness
Nominal
Tolerancl
Grade A min
Grade B.C1.C2. min
0.5-2.5
+0.25-0.00
0.38
0.18
3-4
+0.50-0.00
0.46
0.23
5-6
+0.50-0.00
0.50
0.28
7-9
+0.60-0.00
0.50
0.28
10-12
+0.80-0.00
0.64
0.40
14-18
+0.80-0.00
0.68
0.48
20-30
+1.00-0.00
0.70
0.50

Breakdown Voltage(V)

Grade Lowest Central Value Lowest Individual Value
A
7000
5000
B
4000
2500
C1
2500
1500
C2
1500
800

ACRYLIC COATED FIBERGLASS SLEEVE

  Acrylic coated fiberglass sleeve is made of E-biberglass braided lseeve are baking coated with Acrylic-modified Resin. These sleeve offer reliable dielectric, heat resestance is good, and escellent compatibility with polyester, eposy. Bright- coloured dye ability on sleeving. This is rated for class-F(155℃). It can be used for motors, electrical appliances, electrcal instruments, wireless sets collected stands of wire as well as their protection.

Appearance:
These sleeves' surface is smooth, and bright multicolour.
Dimension:
The standard length is 100020mm(Continuous length may be negotiated)
Note:
The size over 16mm or special requirement may be negotiated.

Inside Diameter and Wall Thickness (Table 1)(mm)

Inside Diametre Wall Thickness
Size Tolerance Minimum Maximun
1-3 0.20 0.20 0.60
4-9 0.30 0.30 0.70
10-16 0.50 0.50 0.80

Performance Index (Table 2)

Performance Index
Breakdown Voltage(even) 4000
2500
1000
Bending at low temperature No cracking or detachment of the coating shell be visible after 60 min at -15℃
Bending after heat treatment No cracking or detachmant of the coating shell be visible after 481hr at 155℃3℃
The other performances Reference to GB7113-7117-86

POLYURETHANE RESIN COATED FIBERGLASS SLEEVE

  Polyrethane fiberglass is made of E-fiberglass braided sleeves are baking coated with polyurethane resin. The coating has high adhesion to the glass braid, retention of dielectric strength is good after aging and physical abuse, dielectric under thermal and electric stress, excellent flexibility and push-back. It offers excellent resistance to oil, good resistance to acid, alkalies and organic solvents. These sleeves are suitable for class-F(155℃) electric motor, electrical apparatus and domestic electrical appliance as well as their protecting device or collected strands of wire.

Appearance:
These sleeves' surfaces are smooth, clear and neat, natural white colour.
Dimension:
The standard length is 100020mm(Continuous length may be negotiated).
Note:
The size over 16mm or special requirement may be negotiated.

Inside Diameter and Wall Thickness (Table 1)(mm)

Inside Diametre Wall Thickness
Size Tolerance Minimum Maximun
1-3 0.20 0.20 0.60
4-9 0.30 0.30 0.70
10-16 0.50 0.50 0.80

Performance Index (Table 2)

Performance Index
Breakdown Voltage(even) 4000
2500
1000
Bending at low temperature No cracking or detachment of the coating shell be visible after 60 min at -15℃
Bending after heat treatment No cracking or detachmant of the coating shell be visible after 481hr at 155℃3℃
The other performances Reference to GB7113-7117-86

Copyright 2014 cgstape.

All rights reserved.

CREATIVE GLOBAL SERVICES INC.
Address:  5-70 Ironside Crescent, Toronto, Canada M1X 1G4
Tel : (416) 292-8258   Fax : (416) 292-1289
E - mail :  info@cgstape.com